DOMAMID® A1-108-N1-N
DOMAMID® A1-108-N1-N is a low viscosity, unreinforced Polyamide 6 compound.General Properties
| Parameter | Value | Testing method |
| Density | 1.12 g/cm³ | ISO 1183/A |
| Melt volume rate – MVR (275°C / 5 kg) | 280 cm³/10 min | ISO 1133 |
| Colour | Nature |
Mechanical Properties (Dry as Molded)
| Parameter | Value | Testing method |
| Tensile modulus (v = 1 mm/min) | 3200 MPa | ISO 527-1A |
| Yield stress (v = 5 mm/min) | 84 MPa | ISO 527-1A |
| Yield strain (v = 5 mm/min) | 3.8 % | ISO 527-1A |
| Stress at break (v = 5 mm/min) | 60 MPa | ISO 527-1A |
| Strain at break (v = 5 mm/min) | 15 % | ISO 527-1A |
| Charpy impact strength notched (+ 23°C) | 5 kJ/m² | ISO 179/1eA |
| Charpy impact strength unnotched (+ 23°C) | N | ISO 179/1eU |
Thermal Properties
| Parameter | Value | Testing method |
| Melting Point | 226°C | ISO 3146 |
| Heat Deflection Temperature: HDT/A (1,8 MPa) | 63°C | ISO 75-2 |
| Heat Deflection Temperature: HDT/B (0,45 MPa) | 155°C | ISO 75-2 |
Transport
The product is packed in 25 kg bags or octabins.
| Per pallet: | Per truck load: | |
| 25 kg bag | approx. 1.0 mt | approx. 20 mt |
| Octabin | approx. 1.0 mt | approx. 20 mt |
Application
- low viscosity injection moulding grade
- fast flowing, easy release
- for thin - walled technical moulded parts